Chemical components | Appearance | Bulk density g/cm³ | Surface area m²/g | Pore volume cm³/g | Crushing strengthN/sphere | Na20% | AI203% | Water adsorption% |
Al2O3·nH2O | Cylinder | 0.55-0.65 | ≥150 | ≥0.50 | ≥100 | ≤0.10 | ≥94 | ≥70 |
Al2O3·nH2O | Clover extrudate | 0.55-0.65 | ≥150 | ≥0.50 | ≥100 | ≤0.10 | ≥94 | ≥70 |
Al2O3·nH2O | Cylinder | 0.5-0.6 | ≥220 | ≥0.60 | ≥90 | ≤0.10 | ≥94 | ≥70 |
Al2O3·nH2O | Clover extrudate | 0.5-0.6 | ≥220 | ≥0.60 | ≥90 | ≤0.10 | ≥94 | ≥70 |
Silicon aluminum composite | Cylinder | 0.5-0.6 | ≥180 | ≥0.50 | ≥100 | ≤0.10 | ≥84 | ≥65 |
Silicon aluminum composite | Clover extrudate | 0.5-0.6 | ≥180 | ≥0.50 | ≥100 | ≤0.10 | ≥84 | ≥65 |
Silicon aluminum composite | Cylinder | 0.55-0.65 | ≥150 | ≥0.45 | ≥90 | ≤0.15 | ≥84 | ≥72 |
Silicon aluminum composite | Clover extrudate | 0.55-0.65 | ≥150 | ≥0.45 | ≥90 | ≤0.15 | ≥84 | ≥72 |
Al2O3·nH2O | Cylinder | 0.70-0.80 | ≥180 | ≥0.40 | ≥80 | ≤0.10 | ≥94 | ≥50 |
Al2O3·nH2O | Ball | ≥0.68 | ≥170 | ≥0.45 | ≥70 | ≤0.20 | ≥94 | ≥65 |
Al2O3·nH2O | Ball | ≥0.68 | ≥170 | ≥0.45 | ≥130 | ≤0.25 | ≥94 | ≥50 |
Al2O3·nH2O | Ball | 0.55-0.60 | ≥250 | ≥0.45 | ≥60 | 0.10-1.00 | ≥94 | ≥60-70 |
Al2O3·nH2O | Clover extrudate | 0.45-0.60 | ≥350 | ≥0.65 | ≥70 | ≤0.10 | ≥95 | ≥80 |
![](http://kehu02.grofrom.com/www.aogecatalyst.com/9d46e48bc09139e0ac079321758990ac.jpg)
![](http://kehu02.grofrom.com/www.aogecatalyst.com/685978932f28420837cd80bd675d4ef4.jpg)
![](http://kehu02.grofrom.com/www.aogecatalyst.com/ffc103b7c95c766f078a44361885ec2e.jpg)
![](http://kehu02.grofrom.com/www.aogecatalyst.com/bdfbf4bd9d65fa5954a32d13855bfe03.jpg)